RPM-MASKING FILM 1

MASKING FILM

Masking film is a special protective high density polyethylene film, with an excellent adhesion of paint as the result of corona treatment and the composition of the raw material with specific additives

 

Technical data:

 

High density polyethylene film Corona treatment + additives Temperature -40 C°+110 C°

  • –  Electrostatic charged with specific generators
  • –  Corona treatment + additives to obtain maximum adhesion of paint Commercial Name COLOUR CM MT Thickness

page1image4033344 page1image4033728 page1image4033920 page1image4034112 page1image4034304 page1image4034496 page1image4034688 page1image4034880 page1image4035072 page1image4035264

Masking Film 5×120 Neutro 500 120 7-8my

page1image4035456 page1image4035648 page1image4035840 page1image4036032

PROPERTIES:

 

Melt Mass-Flow Rate (MFR) (190 °C /2.16 kg) Melt Mass-Flow Rate (MFR) (190 °C /5.0 kg)

Melt Mass-Flow Rate (MFR) (190 °C /21.6 kg) Density (23 °C) *
Tensile Strength at Yield (MD/TD)**

ISO 1133-1 ISO 1133-1

ISO 1133-1 ISO 1183-2 ISO 527-3

g/10 0.08 min
g/10 0.30 min

g/10 9.0 kg/m3 955 MPa 26/25

TEST METHOD

UNIT

TYPICAL VALUE

Tensile Strength at Break (MD/TD)** Tensile Strain at Break (MD/TD)** Elmendorf Tear Resistance (MD/TD)** Dart Drop (F 50)**

Spencer Impact Strength** Vicat Softening Temperature * Shore D Hardness *
OIT (200 °C) *

Typical properties, not to be used as specification.

ISO 527-3 MPa 67/50 ISO 527-3 % 500/600 ISO 6383-2 cN 15/150 ISO 7765-1method A g 243 ASTM D 3420 MPa 120
ISO 306/A 120 °C 126
ISO 868 – 64
EN 728 min 45 page2image3628352 page2image3632192

* * Average mechanical property values of several measurements carried out on standard pressed specimens (ISO 293) conditioned at room

temperature (ISO 291).

** Average mechanical property values of several measurements on film (MD = machine direction, TD = trans direction) thickness of 0.015 mm, blow

up ratio 4:1.

 

RECYCLING:

 

Polyethylene resins are suitable for recycling using modern recycling methods. In-house production waste

should be kept clean to facilitate direct recycling.

 

DISCLAIMER:

 

The information provided in this publication has been compiled to the best of our present knowledge. However, in view of the various applications of polyethylene resins and the equipment used, the processing conditions may differ. The recommendations and data herein are to be construed as informational only and do not relieve users from carrying out their own tests and experiments prior to processing in order to check suitability for a specific use. It is the responsibility of those to whom we supply our products to ensure that any proprietary rights and existing laws and legislation are observed. Our products are under continuous development, therefore we reserve the right to change the information presented in this brochure at our own discretion. The REACH statement herein does not constitute legal advice. The REACH statement is provided for informational purpose only